- EN 10083-3: 2006 Steels for quenching and tempering. Technical delivery conditions for alloy steels
- EN 10269: 1999 Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
- EN 10250-3:2000 Open steel die forgings for general engineering purposes Alloy special steels
China 30CrNiMo8-Alloy steel is used for automotive and general components which require high demands on strength and toughness and good hardenability. It is especially suitable for heavy-duty parts in the aviation, automotive and military industries.
Applications of 30CrNiMo8: For permanently stressed components with large cross sections for automotive and mechanical engineering. For economic performance under severe dynamic stress, parts must be designed for optimum strength or toughness.
C | Si | Mn | Ni | P | S | Cr | Mo |
0.26 – 0.34 | max 0.4 | 0.5 – 0.8 | 1.8 – 2.2 | max 0.025 | max 0.035 | 1.8 – 2.2 | 0.3 – 0.5 |
EU | Germany | Japan | France | England | China | Russia | Inter |
EN | DIN,WNr | JIS | AFNOR | BS | GB | GOST | ISO |
30CrNiMo8 | 30CrNiMo8 | SNCM431 | 30CND8 | 823M30 | 30Cr2Ni2Mo | 3KH3M3F | 31CrNiMo8 |
Surface Finish | Size Tolerance | Length |
Black For Forged condition | (0,+5 ~ +8mm) | Multiple Length/Fixed Length |
Black For Rolled condition | (0,+1mm) | |
Rough Turned | (0,+3mm) |
- Tensile Strength:min 520 N/mm2
- Yield Strength:min. 350 N/mm2
- Elongation:min.11 %(l)
- Kv-Imapct value:min.45J (l)
- +A Soft annealed/Soft annealing
- +N Normalized/Normalizing
- +QT Quenched and Tempered
- +U Untreated
- +SR Stress Relieved
Normalizing:870℃-880℃,Cool in air
Soft Annealing:650℃-700℃,Cooling 10℃ per hour in furnace,max. 248 HB
Stress Relieving:50°C under the temperature of tempering
Hardening:830 – 860°C,oil or polymer,840-850°C,water
Tempering:540°C – 660°C, cool in still air
Drawn and hot-rolled bars, flat bars 30CrNiMo8, 1.6580
Forgings and forged bars in grade 30CrNiMo8, 1.6580